25 Micron Cell Phone Cases / Photo Lamination Film Fast Delivery NEI Brand
Cell Phone Cases / Photo Lamination Film Fast Delivery NEI Brand
Glossy Specifications:
| TYPE | THICKNESS (micron) |
| GLOSSY | TOTAL | BASE | EVA |
| 17 | 12 | 5 |
| 18 | 12 | 6 |
| 20 | 12 | 8 |
| 22 | 12 | 10 |
| 23 | 15 | 8 |
| 25 | 15 | 10 |
| 27 | 15 | 12 |
| 30 | 15 | 15 |
| 42 | 28 | 14 |
| WIDTH (mm) | 200 ~ 2210 |
| LENGTH (m) | 100 ~ 8000 |
| PAPER CORE | 25.4mm(1 inch) / 76mm (3 inch) |
| BONDING | ≤2 |
| CORONA TREATED | Double side |
| SURFACE TENSION | 38 Dyne/cm ≤ 42 Dyne/cm |
| LAMINATION TEMP. | 90±10°C |
| ROLLER PRESSURE | 10 ~ 20Mpa |
| LAMINATION SPEED | 20 ~ 70M |
Matte Specifications:
| TYPE | THICKNESS (micron) |
| MATTE | TOTAL | BASE | EVA |
| 17 | 12 | 5 |
| 18 | 12 | 6 |
| 20 | 12 | 8 |
| 22 | 12 | 10 |
| 23 | 15 | 8 |
| 25 | 15 | 10 |
| 27 | 15 | 12 |
| 30 | 15 | 15 |
| 43 | 28 | 15 |
| WIDTH (mm) | 200 ~ 2210 |
| LENGTH (m) | 100 ~ 8000 |
| PAPER CORE | 25.4mm(1 inch) / 76mm (3 inch) |
| BONDING | ≤2 |
| CORONA TREATED | Double side |
| SURFACE TENSION | 38 Dyne/cm ≤ 42 Dyne/cm |
| LAMINATION TEMP. | 90±10°C |
| ROLLER PRESSURE | 10 ~ 20Mpa |
| LAMINATION SPEED | 20 ~ 70M |
Description:
The hot pressed composite film has an extruded coating surface of low-temperature molten resin, which allows the film to be laminated onto paper products through heat and pressure. Various surface treatments can increase the value of printed surfaces.
The glossy BOPP hot press film provides a shiny colored finish. Its use can improve the appearance and increase the lifespan of all laminated printed materials. Matte BOPP hot press film provides a matte finish on the surface of printed materials to prevent fingerprints and stains. Compared to glossy hot pressed films, matte films can be stored for a longer period of time.
BOPP hot press film has excellent performance characteristics and low price, making it an ideal choice for various printed and non printed paper and cardboard, including book covers, cosmetic packaging, magazines, documents, shopping bags, diaries, etc.
Applications:
Album, phone case, USB cable packaging, headphone packaging, phone accessory packaging, etc
Why chooses NEI BOPP thermal lamination film?
1. Environmentally friendly: Due to the use of non solvent adhesives, it is non-toxic, odorless, or free of benzene. During the lamination process, no toxic gases or volatile substances are emitted, which is harmless to human health. In addition, it is easier to recover than water-based laminated membranes because the membrane and paper can be easily separated.
2. Operational safety: The use of non solvent adhesives eliminates fire hazards caused by the use and storage of flammable solvents.
3. Excellent performance: Compared with wet lamination, thermal lamination improves the color saturation and brightness of printed materials. Has strong powder absorption ability and adhesion. In addition, it can effectively prevent foaming or separation from the printed material during the lamination process. Due to its strong adhesive ability and surface tension, it can be used in subsequent processes, including spot UV, hot stamping, die-cutting, indentation, and other processes.
4. Easy handling: Once the required temperature and pressure is met, lamination can be easily operated. No other special technique is required.
5. High efficiency: No waste of film, no mixing of adhesive solvents, no need for UV heating lamps (drying systems), greatly reducing production and labor costs. Therefore, it also saves production space.
6. Wide adaptability: widely applicable to different types of SMT machines, including wet and dry SMT machines. If using a wet laminating machine, only minor adjustments need to be made to the machine.
Why chooses NEI?
1. Since 1995, NEI has had professional experience in film industry, so we have good quality control and after-sales service to support you.
2. With 10 years of export experience, we have a good reputation in many countries, including South America, North America, the Middle East, Asia, Africa, Oceania, and so on.
3. Compared with other thermal lamination film, our EVA glue is 100% imported from Korea and it ensures the adhesiveness of our film.
4. We can customize the size and thickness according to customer requirements. Tags can also be customized.
5. Rapid production and delivery.
6. Widespread hot pressed film and special thin film.
Special Instruction:
1. It is recommended to composite the NEI BOPP hot pressed film under roller temperature of 85-110 ℃ and roller pressure of 10-20 Mpa. However, the optimal conditions depend on the speed and dimensional stability of the selected laminating machine.
2. It is recommended to dry the printed surface thoroughly before laminating and cool one surface thoroughly before laminating onto other surfaces.